Analisis Pengaruh Nilai Variasi Temperatur Tempering Baja S50C Sebagai Bahan Pisau Mesin Pencacah Plastik

ariyanto ariyanto; Eko  Yudo; Adyu Arya Nicola

doi:10.33504/manutech.v16i01.292

Authors

ariyanto ariyanto polman babel
Eko Yudo
Adyu Arya Nicola

DOI:

https://doi.org/10.33504/manutech.v16i01.292

Keywords:

Heat treatment, Steel S50C, Optimization, Tempering

Abstract

S50C steel is a steel with a carbon content of 0.497 - 0.53% tensile stress of at least 630 mpa. When viewed from the carbon content of the S50C material, this steel is included in medium carbon steel. The carbon range contained in medium carbon steel is between 0.3%C-0.6%C. The minimum requirement for the amount of carbon in steel that can be hardened is greater than 0.3%. By referring to the amount of carbon contained in S50C steel, it can be said that S50C steel can be hardened process. The hardening process is carried out at a temperature of 800 ⁰ C, a temperature of 840 ⁰ C and a temperature of 8800 C, with cooling media being salt water, oil and seawater. After the hardening process is carried out the tempering process at a temperature of 100 ⁰ C, 200 ⁰ C 300 ⁰ C, 400 ⁰ C and 500 ⁰ C,the whole heating process uses an electric oven. The overall parameters of the hardening process are optimized using the Taguchi method. Obtained optimal parameter values at a temperature of 880 ⁰C with a brine-water cooling medium. The average hardness obtained before the tempering process was 56.84 HRC and the highest tempering result was 55.95 HRC the lowest result was 35.15 HRC.

Downloads

Download data is not yet available.

References

B. george S, C. Henry R dan V. John A, “carbon steel,” dalam Materials Handbook, p. 171.

D. D. Y. N. ,. A. R. a. A. S. Juliansyah, “Peningkatan Ketangguhan Impact Pisau Pemotong Rumput Dengan Perlakuan Panas Dengan Menggunakan Media Pendingin Radiator Dan Udara,” J. Renew. Energy Mech., pp. 17-26, 2019.

Meli, G. S. Lubis dan R. A.Wicaksono, “Analisa Pengaruh Heat Treatment Nilai Uji Kekerasan Pada Mata Pisau Mesin Pencacah Botol Limbah Plastik,” Jurnal Teknologi Rekayasa Teknik Mesin (JTRAIN) , vol. 3, pp. 27-31, 2022.

M. . A. Jaelani , M. F. Sidiq dan G. R. Wilis , “Analisa Penguatan Mata Pisau Mesin Pencacah Sampah Organik Dengan Proses Heat Treatment Bertingkat,” CRANKSHAFT,, vol. 4, pp. 93-102, 2021.

Sumpena, H. Hb. Sukarjo, W. dan S. S. Pramana, “Analisa Kekerasan dan Keausan Cylinder Sleeve dari Besi Cor Kelabu,” Jurnal Engine: Energi, Manufaktur, dan Material, vol. 5, pp. 97-103, 2021.

L. H. Vlack, Elements of Materials Science and Engineering, Jakarta: Erlangga, 1986.

H. Mustofa, H. Supriadi dan Z. , “Pengaruh Temperatur Tempering Terhadap Kekerasan dan Struktur Mikro Baja AISI 1045 Yang Diquenching Dalam Media Pendingin Tersirkulasi,” FEMA, vol. 8, pp. 6-16, 2020.

L. Jiangyin Xingcheng Special Steel Works Co., “Quality Certificate,” Jiangyin, 2020.

I. Soejanto, Desain Eksperimen dengan Metoda Taguchi, Yogyakarta: Garaha Ilmu, 2009.

N. Iriawan dan S. P. Astuti, Mengolah Data Statistik Dengan Mudah Menggunakan MInitab 14, Yogyakart: ANDI, 2006.

M. Andreansyah, R. D. Anjani dan V. Naubnome, “Pengaruh Proses Heat Treatment (Quenching dan Tempering) Terhadap Kekerasan dan Struktur Mikro Baja Karbon Menengah,” Serambi Engineering, vol. IX, pp. 64-72, 2024.

R. Naibaho, “Analisis Struktur Mikro Dan Kekerasan Terhadap Perbedaan Media Pendingin Pada Proses Pengerasan Baja,” ATDS SAINTECH , vol. 2, pp. 12-20, 2021.

A. R. Fachrudin dan . F. A. Frida Astuti, “Analisis Proses Hardening terhadap Kekerasan Baja SKS 3 dengan Variasi Temperatur dan Media Pendingin,” Jurnal Pendidikan dan Teknologi Indonesia (JPTI), vol. 3, pp. 109-115, 2023.

S. Pranata, A. T. Husni dan R. Afriany, “Pengaruh Variasi Suhu Tempering 200oC 400oC 600oC Terhadap Kekerasan Dan Ketangguhan Baja JIS G4801 Sup 9,” TEKNIKA, pp. 216-224, 2020.

Khalid, Khardiman dan N. Viktor, “Pengaruh Variasi Temperatur Tempering Terhadap Sifat Mekanik dan Sifat Fisik Baja AISI 1045 Sebagai Bahan Pisau Mesin Pencacah PLastik,” Jurnal Ilmiah Teknik Mesin, vol. 12, pp. 19-25, 2020.

S. Mahardika, “Analisa Rekayasa Sifat Mekanik Baja Aisi 4140 Dengan Variasi Suhu Tempering Untuk Meningkatkan Keuletan Dan Kekerasan Material,” Mekanova, pp. 64-69, 2020.